An Investigation on Wear Resistance of SiCp-Reinforced Aluminium Composites Produced by Mechanical Alloying Method
Küçük Resim Yok
Tarih
2010
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Walter De Gruyter Gmbh
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, Al-SiCp composites were produced by a mechanical alloying method using SiCp powders up to 20 vol% as a reinforcement. The produced compositions were cold pressed at 630 M Pa with a single action and sintered at 560 degrees C for minutes under Ar gas atmosphere The experimental result showed that the reinforcement phase SiCp was homogeneously dispersed in the Al matrix and the interface between Al matrix and SiCp was well formed. Wear tests were carried out under dry sliding conditions using a pin-on-disk type testing machine at three different loads of 10N, 25N and 50N and at a sliding speed of 2.08 m/s Total sliding distance was selected as 400, 800, 1200 and 1600 m. After wear tests, the wear amount was determined by measuring the weight and dimension of specimens It was seen that the wear rate increased with increasing the applied load from 10N to 50N, sliding distance and decreased with increasing SiCp amount Microstructures and worn surface of Al-SiCp composites were investigated by SEM.
Açıklama
Anahtar Kelimeler
Al-SiCp composites, Mechanical Alloying, Wear Resistance
Kaynak
Science and Engineering of Composite Materials
WoS Q Değeri
Q4
Scopus Q Değeri
Cilt
17
Sayı
1