Effects of boron compounds on the bonding strength of phenol-formaldehyde and melamine-formaldehyde adhesives to impregnated wood materials
Küçük Resim Yok
Tarih
2006
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Taylor & Francis Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Wood materials are increasingly being used in the construction of structural beams, sports equipment, etc. This study was carried out to determine the bonding strength of phenol-formaldehyde (PF) and melamine-formaldehyde (MF) adhesives to impregnated wood materials. For this purpose, brutia pine (Pinus brutia Ten) and elm (Ulmus compestris L.) woods were impregnated with borax (Bx), boric acid (Ba), Bx + Ba (wt:wt 50:50%), di-ammonium phosphate (D), [D + (Bx + Ba)]/ (50 + (25 + 25%), w/w) and Tanalith-C 3310 (T-C 3310) using the vacuum method according to ASTM-D 1413-76. The effects of wood species, impregnating material and type of adhesive on the bonding strength were determined. The highest shear strength (11.09 N/mm(2)) was obtained from elm wood control (i.e., without any impregnating materials) samples with MF; thus, the impregnation process negatively affected the adhesive bonding strength. Impregnating materials, especially those containing oily or similar solutions such as T-C 3310, are not advised for wood elements which are subjected to shear.
Açıklama
Anahtar Kelimeler
melamine-formaldehyde, phenol-formaldehyde, boron compounds, shear strength, impregnating materials
Kaynak
Journal of Adhesion Science and Technology
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
20
Sayı
10