Yorur, H.Yapici, F.Esen, R.2024-09-292024-09-292013978-953292031-4https://hdl.handle.net/20.500.14619/9856Croatian Chamber of Economy; Croatian Chamber of Engineers of Forestry and Wood Technology; Croatian Forest Research Institute; Croatian Forests d.o.o.; et al.; Ministry of Entrepreneurship and Crafts24th International Scientific Conference: Wood is Good - User Oriented Material, Technology and Design -- 18 October 2013 -- Zagreb -- 115961This study was carried out to determine the effects of using cast-polyamide on modulus of rupture (MOR) and modulus elasticity (MOE) of oriented strand board (OSB) which were produced in four different conditions. Firstly, control panels were manufactured, and also OSB panels produced by adding cast-polyamide with 20 % - 30 % ratio compare with weight of oven dry wood particle both out layer and inner layer. Phenol formaldehyde was used at 6 % ratio. Strands were used to the production of panels made up 50 % of core layer and 50 % of outer layers. Test panels were pressed in 6 min., 40 kg/cm2 press pressure and 185±3°C press temperature by aiming for a target density of 0.67 g/cm3. The values of modulus of rupture and modulus elasticity were determined by using according to related standard.eninfo:eu-repo/semantics/closedAccessCast-polyamideMOE valueMOR valueOriented strand boardPhenol-formaldehydeThe effects of cast-polyamide on the modulus of rupture and modulus elasticity of oriented strength board (OSB) Manufactured from Scotch PineConference Object2-s2.0-84946616190182N/A179