Guven, SedatAltin Karatas, MeltemGokkaya, HasanAkinay, Yuksel2024-09-292024-09-2920220954-40622041-2983https://doi.org/10.1177/09544062211069864https://hdl.handle.net/20.500.14619/6451In this study, electropolishing and two different heat treatments were applied to wires made of superelastic nickel-titanium (NiTi) shape-memory alloy (SMA) and their mechanical properties and stress-induced deformations were investigated. In experimental studies, cryogenic and aging heat treatments were applied to NiTi SMA wire samples and tensile test experiments were carried out to determine the effect of the heat treatments on their mechanical properties. Following the tensile test experiments conducted at room temperature (23 degrees C), the study investigated changes in the elemental composition, fracture modes, micro cracks, and phase structures and in the mechanical properties formed in the fracture region. Intermetallic phase structures (Ti2Ni, Ni3Ti, and Ni4Ti3) were observed in the X-ray diffraction (XRD) analyses. It was concluded that the aging heat treatment had directly affected the reduction in hardness. In particular, in samples without the aging heat treatment, a stress-induced decrease in the Ni and Ti ratios and an increase in the carbon (C) ratio were observed in the chemical composition of the fracture surface of the superelastic NiTi SMA wires. It was determined that the changes in the chemical composition caused by stress had affected the mechanical properties negatively. In the fractography of the NiTi SMA wires, the samples exhibited mostly ductile fracture behavior with small dimples.eninfo:eu-repo/semantics/closedAccessSmart materialsshape-memory alloysmechanical propertiescryogenic treatmentagingArticle10.1177/095440622110698642-s2.0-85125095100675912Q26752236WOS:000759218500001Q3