Erden, Mehmet AkifTasci, Muhammed Taha2024-09-292024-09-2920161302-09002147-9429https://doi.org/10.2339/2016.19.4.611-616https://hdl.handle.net/20.500.14619/7056In this work, the effect of Ni (wt. % 2-3-5) on the microstructures and tensile behaviours of Fe matrix metarials including graphite 0.55 wt. % and (Nb-V) 0.15 wt. % were investigated. The samples pressed at 750 MPa were produced by sintered at 1350 degrees C temperature in the argon atmosphere for 1 h. The microstructure of the producted PM steels was characterised by optic microscope, SEM and EDS. Results indicated that 5 wt. % Ni added PM steel showed the highest values in yield strength (YS) and ultimate tensile strength (UTS).trinfo:eu-repo/semantics/closedAccessPowder metallurgypowder metallurgy steelsNimicrostructuremechanical propertiesArticle10.2339/2016.19.4.611-616616461119WOS:000447835300027N/A