Yazar "Özcan, Cemal" seçeneğine göre listele
Listeleniyor 1 - 8 / 8
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Öğe Determination of combustion properties of heat treated wood materials(2021) Özcan, Cemal; Gündüz, GökhanStudies on heat-treated wood are mostly focused on physical and mechanical properties. There is no sufficient study on combustion properties of heat-treated wooden material. In this study, combustion properties of heattreated wooden material were determined. According to results of combustion, mass reduction in heat-treated wooden material less than non-heat-treated wood material. Temperature values of the heat-treated wooden material are higher than control samples. During combustion test, also, it was noticed that the amount of released gases such as carbon monoxide (CO), nitrogen oxide (NO) and oxygen (O2) values in heat-treated wooden material are higher than control ones in general.Öğe The effect of liquid nitrogen on retention in uludağ fir wood treated with boric acid and borax(2012) Kurt, Seref; Özcan, Cemal; Lıkos, Erkan; Korkmaz, MustafaIn this study, the effect of liquid nitrogen on retention of Uludağ Fir wood after exposure to boric acidand borax was determined. Before treating with liquid nitrogen, specimens were conditioned to 4 differentmoisture contents (oven dry, 12%, 28%, and green). Liquid nitrogen treated specimens for 1 hour, 4 hoursand 10 hours. Then, all specimens were conditioned to 12% moisture content (MC). Test specimens wereexposed to chemicals such as borax and boric acid for three times: short (2 min), normal (1 hour) and long (1week). Dipping method was used for the impregnation process. For control, specimens were treated withborax and boric acid without treating with liquid nitrogen. Consequently, there is a linear relationshipbetween moisture content and retention. Since moisture content increases the amount of retention increasesas well.Öğe The effects of exposure to sea water steam on thermal conductivity of varnished fir wood(2012) EŞen, Rasit; Özcan, Cemal; Lıkos, Erkan; Özkan, Osman EmreIn this study, the thermal conductivity of varnished fir wood exposed to sea water steam wasinvestigated. For this purpose, test samples were coated by using varnishing goldspar (polyurethanevarnish), original (synthetic varnish), perfection (polyurethane varnish), and schooner varnishes (syntheticvarnish). After applying furnished process, samples were exposed to sea water steam during 6, 24, 60, and96 hours. It was found that the vapour application has decreased the chemical and physical structure oftest material. The thermal conductivity test was performed based on the ASTM C 1113-99 hot-wiremethod.Öğe The effects of fire retardants paint on combustion properties of fir wood(2012) Özcan, Cemal; EŞen, Rasit; Lıkos, Erkan; Kurt, Seref; Yapıcı, FatihThe effects of fire retardants paint on combustion properties of fir (Abies bornmülleriana M.) wereexamined. For this purpose, fire retardants paint were applied on the surface of test sample according tocompany s suggestions. The combustion test was performed according to the ASTM-E 69 standard. Themass reduction, release of gasses (CO, NO, O 2 ), and temperature differences of samples were determinedfor each 30 seconds during combustion. It was observed that the highest mass reduction occurred in fir woodwith fire retardant paintÖğe The effects of humidity on thermal conductivity of fir wood(2012) EŞen, Rasit; Lıkos, Erkan; Özcan, Cemal; Korkmaz, Mustafa; Kılınç, IzhamIn this study it was aimed to describe the effects of different humidity on thermal conductivity ofUludag Fir (Abies bornmülleriana M.). The lowest thermal conductivity of 0.0910 Kcal/mh°C wasobtained from oven-dry samples. The highest thermal conductivity of 0.1904 Kcal/mh°C was obtained incompletely wet samples. Consequently, oven-dry wood samples could be used as insulation material.Öğe Emprenye ve üst yüzey işlemi uygulanmış ceviz ağaç malzemenin yanma özelliklerinin belirlenmesi(2019) Özcan, CemalBu çalışmada, farklı kimyasallarla emprenye edilen ceviz (Juglans regia L.) ağaç malzemede yangın geciktirici üst yüzey işlemlerinin yanma direncine etkileri incelenmiştir. Bu amaçla emprenye maddesi olarak borik asit, boraks, sodyum silikat, diamonyum fosfat, amonyum sülfat ve çinko klorür kullanılmıştır. Üst yüzey malzemesi olarak ise yangın geciktirici boya ve nano özellikli yangın geciktirici vernik kullanılmıştır. Yanma deneyleri, ASTM-E 69 standartlarına göre geliştirilen bilgisayar kontrollü ağaç malzeme yanma düzeneğinde gerçekleştirilmiştir. Baca gazı analizi Testo 350M/Xl gaz analiz cihazıyla gerçekleştirilmiştir. Bu sayede karbon monoksit (CO), azot oksit (NO), oksijen (O2) ve baca sıcaklığı değerleri elde edilmiştir. Sonuç olarak, ceviz ağaç malzemeye yangın geciktirici boya ile üst yüzey işlemi uygulamanın, kullanılan tüm emprenye maddelerinden ağırlık kaybını azaltmada daha etkili olduğu gözlemlenmiştir. Bununla birlikte, nano özellikli yangın geciktirici vernik ile üst yüzey işlemi uygulamanın boraks, borik asit, sodyum silikat ve diamonyum fosfat ile emprenye etmekten daha az ağırlık kaybına yol açtığı gözlemlenmiştir.Öğe Isıl işlemin meşe (quercus petraea l.) Ağaç malzemede yapışma direncine etkileri(2012) EŞen, Rasit; Özcan, CemalIsıl işlem yöntemi, kimyasal maddeler kullanmadan ağaç malzemenin korunması için yapılan bir koruma yöntemidir. Buçalışmada meşe (Quercus petraea L.) ağaç malzemeden elde edilen deney örnekleri 170,190 ve 210 ºC sıcaklıklarda 2,6 ve 10saat süre ile ısıl işleme maruz bırakılmıştır. Isıl işlem yapıldıktan sonra deney örnekleri poliüretan (PUR), fenol-formaldehit (FF),melamin-üre-formaldehit (MUF) ve melamin-formaldehit (MF) tutkalları kullanılarak yapıştırma direnci belirlenmiştir. Sonuçolarak ısıl işlem yapışma direncini olumsuz etkilemektedir. En yüksek yapışma direnci melamin formaldehit tutkalı ileyapıştırılan 2 saat süre ile 170 ºC sıcaklıkta ısıl işlem gören meşe ağaç malzemede belirlenmiştir. En düşük yapışma direnci 210ºC sıcaklıkta 10 saat süre ile ısıl işlem görmüş meşe ağaç malzemenin poliüretan tutkal ile yapıştırılan örneklerden elde edilmiştir.
