Evolution of Microstructure, Mechanical Properties, and Corrosion Resistance of Mg-2.2Gd-2.2Zn-0.2Ca (wt%) Alloy by Extrusion at Various Temperatures
(Mdpi, 2023) Zengin, Hueseyin; Ari, Soner; Turan, Muhammet Emre; Hassel, Achim Walter
The current investigation involved casting the Mg-2.2Gd-2.2Zn-0.2Ca (wt%) alloy (GZX220) through permanent mold casting, followed by homogenization at 400 degrees C for 24 h and extrusion at 250 degrees C, 300 degrees C, 350 degrees C, and 400 degrees C. Microstructure investigations revealed that alpha-Mg, Mg-Gd, and Mg-Gd-Zn intermetallic phases were present in the as-cast alloy. Following the homogenization treatment, a majority of these intermetallic particles underwent partial dissolution into the matrix phase. alpha-Mg grains exhibited a considerable refinement by extrusion due to dynamic recrystallization (DRX). At low extrusion temperatures, higher basal texture intensities were observed. The mechanical properties were remarkably enhanced after the extrusion process. However, a consistent decline in strength was observed with the rise in extrusion temperature. The corrosion performance of the as-cast GZX220 alloy was reduced by homogenization because of the lack of corrosion barrier effect of secondary phases. A significant enhancement of corrosion resistance was achieved by the extrusion process.