Yazar "Sonmez, A." seçeneğine göre listele
Listeleniyor 1 - 3 / 3
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Effects of application methods and species of wood on color changes of varnishes(Academic Journals, 2009) Budakci, M.; Ozcifci, A.; Cinar, H.; Sonmez, A.In this study, the color effects of wood materials to coloring with different application methods (brush, roller sponge and spray gun) and waterborne varnishes were investigated according to ASTM-D 2244. For this purpose, the experimental samples of Scots pine (Pinus silvestris L.), oriental beech (Fagus orientalis L.) and oak (Quercus petreae L.), which are commonly used woods in the carpentry and furniture industry in Turkey, were prepared and varnished with one and two-pack waterborne varnishes in accordance with ASTM D 3023. According to the result of the research, significant color changes in coloring as red and yellow tones on the sample surfaces of varnished wood materials were found. The highest color change was obtained in the samples of oak, when varnished with brush and spray gun while the lowest value was obtained in roller sponge in respect to the application methods for waterborne varnishes. However, the application method of spray gun for self crosslinked polyurethane, topcoat-clear, (SCPt) gave the highest metric chroma value among the three different application methods. © 2009 Academic Journals.Öğe Effects of some environmentally-friendly fireretardant boron compounds on modulus of rupture and modulus of elasticity of wood(2009) Toker, H.; Baysal, E.; Simsek, H.; Senel, A.; Sonmez, A.; Altinok, M.; Ozcifci, A.This study was designed to determine some mechanical properties such as modulus of rupture (MOR) and modulus of elasticity (MOE) of wood treated with some environmentally-friendly fire-retardant boron compounds. Sodium perborate (SP) boric acid, (BA), and borax (BX) were used as boron compounds. Wood specimens were prepared from Calabrian pine (Pinus brutiaTen.) and beech (Fagus orientalis Lipski) wood. Before MOR and MOE tests, wood specimens were impregnated with aqueous solutions (1,2, 3,4, 5, and 6 %) of borates according to ASTM D 1413-76. Our results showed that MOR values of wood specimens treated with borates were lower compared to untreated control specimens. The MOR and MOE values of wood specimens were the lowest for treatments with SP followed by BX and BA, respectively. In general, the higher concentration levels of borates, the lower MOR of wood resulted.Öğe An investigation on compression parallel to grain values of wood impregnated with some boron compounds(2008) Toker, H.; Baysal, E.; Ozcifci, A.; Altinok, M.; Sonmez, A.; Yapici, F.; Altun, S.This study was carried out to determine compression strength parallel to grain of wood impregnated with some boron compounds. Sodium perborate (SP) boric acid, (BA), and borax (BX) were used as boron compounds. Wood specimens were prepared from Calabrian pine (Pinus brutia Ten.) and beech (Fagus orientalis L.) wood. Before compression test parallel to grain, wood specimens were impregnated with aqueous solutions (1, 2, 3, 4, 5, and 6 %) of boron compounds according to ASTM D 1413(1976). Results showed that compression strength parallel to grain values ofwood specimens treated with boron compounds were lower compared to untreated control specimens. Borate treatments reduced compression strength parallel to grain of wood in significant level compared to untreated control. The compression strength parallel to grain values ofwood specimens were the highest for untreated control specimen followed by BA, BX, and SP treated wood specimens, respectively. In general, our results showed that the higher concentration levels of boron compounds, the lower compression strength parallel to grain values of wood resulted.