dc.description.abstractIn this paper, the influence of the aging process on the microstructure and machinability of Corrax Steel was investigated for four samples: a solution heat-treated (A0) and three samples aged at 400 degrees C (A4), 525 degrees C (A5.25) and 600 degrees C (A6) for four hours. The effect of aging temperature on hardness was examined. Machining tests were carried out using a CNC lathe with a multi-layer coated PVD (AlTiN) cutting tool, at various cutting speeds (50, 100, 150, 200, 250, 300, 350m/min) with constant feed rate (0.1mm/rev) and 1mm constant cutting depth. The microstructure was investigated using an optical microscope and EDS attached SEM. The effect of aging on reverted austenite formation was also evaluated. In order to understand the changes in surface topology, cutting forces and vibrations were measured. With increasing aging temperature, the lath martensite was transformed to plate martensite because of the formation of precipitates and reverted austenite. Aging at different temperatures increased hardness up to 58%, cutting forces up to 117% and surface roughness up to 450%. The results describe the effect of the aging treatment on cutting forces, surface topology, tool wear and vibrations.en_US
dc.description.sponsorshipScientific Research Projects Department of Karabuk University (BAP) [KBUBAP-18-KP-145]en_US
dc.description.sponsorshipThis research was supported by the Scientific Research Projects Department of Karabuk University (BAP) with Project No KBUBAP-18-KP-145.en_US
dc.identifier.endpage5174en_US
dc.identifier.issn2241-4487
dc.identifier.issn1792-8036
dc.identifier.issue1en_US
dc.identifier.startpage5168en_US
dc.identifier.urihttps://hdl.handle.net/20.500.14619/8592
dc.identifier.volume10en_US
dc.identifier.wosWOS:000512366900013en_US
dc.identifier.wosqualityN/Aen_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.language.isoenen_US
dc.publisherEos Assocen_US
dc.relation.ispartofEngineering Technology & Applied Science Researchen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectdry turningen_US
dc.subjectcorraxen_US
dc.subjectcutting forceen_US
dc.subjectsurface roughnessen_US
dc.subjectvibrationen_US
dc.titleAging Effect on Microstructure and Machinability of Corrax Steelen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu