Recovery of iron from high-iron hot rolled mill scales by direct reduction technique
Küçük Resim Yok
Tarih
2021
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
In this study, the integrated iron and steel plant mill scales were prepared to concentrate in different ratios by blending with hematite character ore. Carboxymethyl cellulose (CMC) was used as a binder and coke will be used as a reductant. The calcite was added in such a way that the basicity ratio is 0.7. The pelletizing machine was pellet the blends containing the mill scales at different ratios and then drying at a temperature of 150 °C. 28 kg/pellet compressive strength was obtained in the pellets prepared from 100% mill scales. As the amount of ore increased to 75%, 45 kg/pellet was reached with a 50% increase in compressive strength. After compression tests, dried pellets were subjected to reduction at 3 different temperatures (1200, 1300, and 1400 oC), and their reduction degrees were calculated based on oxygen loss. The highest reduction degree (82%) was obtained at 1400 oC from the completely prepared with mill scales.
Açıklama
Anahtar Kelimeler
Kaynak
Düzce Üniversitesi Bilim ve Teknoloji Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
9
Sayı
2