    Hydrogen storage capabilities of ionothermally synthesized covalent triazine frameworks (CTFs)
    (Pergamon-Elsevier Science Ltd, 2023) Ergani, Songul Kaskun; Sonmez, Turgut; Uecker, Jan; Arpa, Beyza; Palkovits, Regina
    Covalent triazine frameworks (CTFs) represent an attractive new type of porous organic compounds demonstrating promising stability, nontoxicity, nitrogen functionalities and adjustable porosity. They have been greatly investigated in various applications; however, the hydrogen storage capacities of CTFs have been poorly described so far. Here, we present hydrogen storage capacities of a series of covalent triazine frameworks based on four different applied monomers (DCP, DCBP, mDCB and pDCB) synthesized via classical ionothermal route (ZnCl2, 400/600 degrees C). Among the synthesized CTFs, DCP shows the highest hydrogen storage capacity of 4.02 wt% at 20 bar, almost two times higher compared to the lowest value of 2.43 wt% for CTF DCBP. Furthermore, the CTF DCP outperforms with a H-2 uptake of 2.95 wt% at 1 bar pressure and 77 K state-of-the-art 2D porous organic polymers and shows very high uptake capability within the reported porous polymer materials. The high hydrogen storage capability of DCP is correlated to the high nitrogen (N) content of 20.4 wt%, high fraction of pyridinic N-sites (50.3%), the largest defect structure, highest crystallinity and microporosity among the synthesized CTFs. The specific surface area (SSA) and the total pore volume (TPV) seem to not have an influential impact on the H(2 )storage capacity as the CTF DCP exhibits the highest H-2 storage capacity with a SSA of 1737 m(2) g(-1) and a TPV of 0.9 cm(3) g(-1), the lowest values among the CTFs.(c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
  • Küçük Resim
    Öğe
    NİTROJENCE ZENGİN KOVALENT TRİAZİN KAFES POLİMERLERİNİN HİDROJEN DEPOLAMA KAPASİTELERİNİN İNCELENMESİ
    (2022-01) Arpa, Beyza
    Kovalent triazin kafesler (KTK) yüksek nitrojen miktarları, termal kararlılıkları ve yüksek kimyasal stabilite özellikleri ile pratik uygulamalar için tercih edilen malzemelerdir. Böylelikle KTK’lar enerji depolama, hidrojen depolama, fotokatalitik sistemler ve pekçok uygulamada yüksek avantaj sağlar. Bu tezin amacı, sentezlenen yüzey alanı geniş nitrojence zengin KTK’ların hidrojen depolama seviyelerinin incelenmesidir. Sentezlenen KTK’ların yapısı BET (yüzey alanı ölçümü analizi), XRD (X ışını difraktometre) ve FT-IR (Fourier dönüşümlü kızılötesi spektroskopi) analizleriyle belirlenmiştir. Yapısı belirlenen KTK’ların yüzey alanları incelenmiş ve hangi koşullar altında (basınç, sıcaklık ve katalizör) hidrojen depolamanın maksimum seviyeye ulaştığı tespit edilmiştir. KTK’ların hidrojen depolama kapasitesinin en üst seviyeye çıktığı ortam koşulu 20 bar basınç altında DCP polimerinde gözlenmiştir. Sentezlenen numuneler arasında en düşük depolama miktarı DCBP polimerinde 1 bar basınç altında %1,27; en yüksek depolama miktarı ise DCP polimerinde 20 bar basınç altında %4,02 oranında ölçülmüştür. Bu deneysel çalışmalardan elde edilen veriler ışığında, sentezlenen kovalent triazin kafeslerin hidrojen depolama miktarları farklı basınçlar altında gösterilmiştir.