Factors Affecting Kinetics of Strain Aging in S275JRC Steel
Küçük Resim Yok
Tarih
2017
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Univ Fed Sao Carlos, Dept Engenharia Materials
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The materials parameter i.e. microstructure as well as the processing factors i.e. aging time and temperature, the amount of plastic deformation, and residual stresses affecting the kinetic of strain ageing in the S275JRC steel were investigated in detail. For this purpose, 5 % pre-strained steel was aged at 160 degrees C for different intervals. The ageing behavior was determined for the as-received (AR) and homogenization & normalizing heat treated (H+N heat treated) conditions. The yield stresses before and after aging process and, the hardness values of the aged steels were considered to calculate strain aging progress. It was shown that a noticeable increase in the yield strength, tensile strength and hardness values was observed for aged AR and H+N heat treated specimens. Moreover, the repetitive increase in the yield and ultimate tensile strength was believed to be a result of strain ageing.
Açıklama
Anahtar Kelimeler
S275JRC steel, static strain ageing, mechanical properties
Kaynak
Materials Research-Ibero-American Journal of Materials
WoS Q Değeri
Q4
Scopus Q Değeri
Q3
Cilt
20
Sayı
1