The effect of Ni addition on microstructure and mechanical properties of cast A356 alloy modified with Sr

Küçük Resim Yok

Tarih

2021

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Redakcia Kovove Materialy

Erişim Hakkı

info:eu-repo/semantics/openAccess

Özet

In this study, casting A356 alloy was pre-alloyed with Ni, and the modification process with Sr was applied by the casting method. The role of Ni on the microstructural and mechanical properties of the produced A356-Ni alloys was investigated. The produced alloys were naturally aged at room temperature for 24 h and artificially aged at 170 degrees C for 10 h. Optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffractometer were used in microstructure studies of the A356-Ni alloys. Tensile tests and hardness measurements were carried out to determine mechanical properties. Statistical analysis of Weibull distribution on the tensile test results revealed that the characteristic ultimate tensile strength increased due to increasing the amount of alloying elements, while the characteristic percentage elongation is decreased. This was because Al-Si-Fe intermetallic decomposition and Al-Si-Fe-Ni intermetallics were formed, primarily, 0.5 and 1.0 % Ni addition. It was also determined that the Al-Si-Fe-Ni intermetallics with a morphology non-sharp corners formed more homogeneous in the microstructure. But in the A356 alloys with the addition of 1.5 % Ni, Al-Si-Fe-Ni intermetallics are formed in coarser morphology. In A356 alloys, aluminium dendrites, Al-Si eutectic between dendrites, Mg2Si precipitates are formed in the structure by ageing. Depending on the amount of Ni added to the A356 alloy, the tensile strength of the alloys containing 0.5 and 1.0 % Ni is increased.

Açıklama

Anahtar Kelimeler

A356 alloy, nickel, microstructure, T6 heat treatment, mechanical properties

Kaynak

Kovove Materialy-Metallic Materials

WoS Q Değeri

Q4

Scopus Q Değeri

Q3

Cilt

59

Sayı

6

Künye