The Effect of TiB2 Content on Wear and Mechanical Behavior of AZ91 Magnesium Matrix Composites Produced by Powder Metallurgy
Küçük Resim Yok
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this research, AZ91 magnesium matrix composites reinforced with three weight fractions (10, 20, and 30 wt.%) of TiB2 particulates were fabricated by powder metallurgy using hot pressing technique. The microstructure, density, hardness, wear, and mechanical properties of the specimens were investigated. Microstructure studies showed that fairly uniform distribution of reinforcements was achieved, but partial agglomeration could be clearly seen at 30 wt.% TiB2. X-ray studies exhibited that phases of Mg, Mg17Al12, and TiB2 were found. As compared to AZ91, the hardness and wear resistance considerably increased with increasing reinforcement content. The presence of TiB2 particles improved 0.2% compressive yield strength and ultimate compressive strength (UCS); however, UCS decreased above 20 wt.% TiB2. Wear mechanisms are oxidative and abrasive.
Açıklama
Anahtar Kelimeler
AZ91, composite, wear, microstructure, TiB2, mechanical behavior
Kaynak
Powder Metallurgy and Metal Ceramics
WoS Q Değeri
Q4
Scopus Q Değeri
Q3
Cilt
57
Sayı
9-10