Investigation on joint properties of AA5754 and AA6013 dissimilar aluminum alloys welded using automatic GMAW

Basit Öğe Kaydı
dc.contributor.authorMercan, E.
dc.contributor.authorAyan, Y.
dc.contributor.authorKahraman, N.
dc.date.accessioned2024-09-29T16:21:11Z
dc.date.available2024-09-29T16:21:11Z
dc.date.issued2020
dc.departmentKarabük Üniversitesien_US
dc.description.abstractAluminum alloys AA5754 and AA6013 were joined using gas metal arc welding (GMAW) and the mechanical, microstructure and corrosion properties of the joints were investigated. The welding process was performed using argon as shielding gas with three different wire feed speeds and welding speeds. Metal wire (ER5356 filler) with a diameter of 1.2 mm was used in the welding process. In order to determine the mechanical properties of the joints, the welded specimens were subjected to tensile and hardness tests. In addition, an electrochemical corrosion test was conducted to determine the corrosion resistance of the specimens. The welding zone of the specimens was characterized via microstructure examination. In the tensile tests, fractures occurred in the weld metal and the heat affected zone (HAZ). However, tensile strength performance of the joints exceeded 90% under the appropriate welding parameters. The corrosion test results showed that the samples with joint defects (insufficient melting) were exposed to corrosion more rapidly than the others. Hardness test results revealed that maximum hardness values were measured at the HAZ of the AA6013 specimen, followed by the weld metal and HAZ of the AA5754 specimen, respectively. Microstructure inspections showed the structures of all the weld metals to be dendritic. © 2019 Karabuk Universityen_US
dc.identifier.doi10.1016/j.jestch.2019.11.004
dc.identifier.endpage731en_US
dc.identifier.issn2215-0986
dc.identifier.issue4en_US
dc.identifier.scopus2-s2.0-85076553135en_US
dc.identifier.scopusqualityQ1en_US
dc.identifier.startpage723en_US
dc.identifier.urihttps://doi.org/10.1016/j.jestch.2019.11.004
dc.identifier.urihttps://hdl.handle.net/20.500.14619/9580
dc.identifier.volume23en_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherElsevier B.V.en_US
dc.relation.ispartofEngineering Science and Technology, an International Journalen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectAA5754en_US
dc.subjectAA6013en_US
dc.subjectAluminum alloysen_US
dc.subjectCorrosionen_US
dc.subjectGMAWen_US
dc.subjectMechanical propertiesen_US
dc.titleInvestigation on joint properties of AA5754 and AA6013 dissimilar aluminum alloys welded using automatic GMAWen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

Scopus İndeksli Yayınlar Koleksiyonu