Effect of heat treatment on the properties of plasma arc welded TRIP800 steel
Küçük Resim Yok
Tarih
2022
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Walter De Gruyter Gmbh
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, the effect of heat treatment applied at various temperatures on the properties of plasma arc welded TRIP800 steel has been examined extensively. For this purpose, the low temperature heat treatment was carried out at -50, -20, and 0 degrees C for 2 h on a set of welded samples. Moreover, the heat treatment process was also applied for 2 h at various temperatures (i.e., 100, 200, 300, 400, 500, 600, 800, and 1000 degrees C) for another group of plasma arc welded TRIP800 steels. In addition, the properties of a set of samples without any heat treatment were determined in as-welded condition for a comparison. The mechanical properties of all samples were determined, and microstructures of samples were evaluated. As a result, the low temperature heat treatment applied at the specified temperatures did not have a significant effect on the ultimate tensile strength, and ductility of the joint but affected the yield strength positively. Besides, the ultimate tensile strength of heat treated samples also diminished with increasing processing temperature. It was found that the yield strength of the heat treatment applied samples showed an increase up to 500 degrees C, while the samples tested at 500 and 600 degrees C showed pronounced yielding behavior.
Açıklama
Anahtar Kelimeler
heat treatment, mechanical properties, microstructure, plasma arc welding, TRIP steels
Kaynak
Materials Testing
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
64
Sayı
11