An Investigation of Mechanical and Wear Performance of TiB2/GNPs-Reinforced ZK60 Mg Matrix Composites Fabricated Via Powder Metallurgy

Basit Öğe Kaydı
dc.authoriddemir, BILGE/0000-0002-3617-9749
dc.contributor.authorMustu, Mustafa
dc.contributor.authorDemir, Bilge
dc.contributor.authorAydin, Fatih
dc.date.accessioned2024-09-29T15:54:32Z
dc.date.available2024-09-29T15:54:32Z
dc.date.issued2023
dc.departmentKarabük Üniversitesien_US
dc.description.abstractIn this study, ZK60 alloy, ZK60/15 wt.% TiB2, and ZK60/15 wt.% TiB2 - 0.5 GNPs composites were prepared by hot pressing. The density, microstructure, hardness, and tribological and compression behavior of the samples were investigated. Microstructure investigations showed that TiB2 particles were generally homogeneously dispersed, but GNPs particles were agglomerated. Under 10 and 40 N loads, the best wear performance was obtained with 15 wt.% TiB2 - 0.5 GNPs and ZK60/15 wt.% TiB2 samples, respectively. Abrasion at low and delamination at high loads were observed as the dominant wear mechanism. According to the mechanical test results, the highest hardness (87.1 HV), compressive yield strength (290.1 MPa) and ultimate compressive strength (379.2 MPa) were obtained for the ZK60/15 wt.% TiB2 composite. Fracture surface investigations showed that the mechanism was cleavage fracture and the presence of crack formations on the surface.en_US
dc.description.sponsorshipKarabuk University Coordinatorship of Scientific Research Projects (KBU-BAP) [FDK-2020-2322]en_US
dc.description.sponsorshipThe authors would like to thank the Karabuk University Coordinatorship of Scientific Research Projects (KBU-BAP) for the financial support of this study with the project number FDK-2020-2322.en_US
dc.identifier.doi10.1007/s11665-022-07382-3
dc.identifier.endpage3541en_US
dc.identifier.issn1059-9495
dc.identifier.issn1544-1024
dc.identifier.issue8en_US
dc.identifier.scopus2-s2.0-85138419689en_US
dc.identifier.scopusqualityQ2en_US
dc.identifier.startpage3527en_US
dc.identifier.urihttps://doi.org/10.1007/s11665-022-07382-3
dc.identifier.urihttps://hdl.handle.net/20.500.14619/4117
dc.identifier.volume32en_US
dc.identifier.wosWOS:000857926400002en_US
dc.identifier.wosqualityQ3en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherSpringeren_US
dc.relation.ispartofJournal of Materials Engineering and Performanceen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectcompressionen_US
dc.subjecthot pressingen_US
dc.subjecthybrid compositeen_US
dc.subjectwearen_US
dc.subjectZK60 alloyen_US
dc.titleAn Investigation of Mechanical and Wear Performance of TiB2/GNPs-Reinforced ZK60 Mg Matrix Composites Fabricated Via Powder Metallurgyen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu