Diagonal Tension Performance of Impregnated Woodworking Corner Joints
Küçük Resim Yok
Tarih
2022
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Zagreb Univ, Fac Forestry
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
center dot In this study, the effects were examined of wood species, processing types and processing time on diagonal tension performance of woodworking corner joint with double tenon and mortise. Test samples were prepared by using Scots pine (Pinus sylvestris Lipsky), sessile oak (Quercus petreae Lipsky) and black locust (Robinia pseudoacacia L.). Poly vinyl acetate (PVAc) adhesive was used to join the tenon and mortise corner joints. The samples were impregnated by using the method of immersion for 20 and 40 min with a mixture of wax / linseed oil (3 % paraffin, 10 % linseed oil, 87 % white spirit) and Imersol-Aqua. The test of diagonal compression was used to test 120 samples. In this study, the minimum strength decrease of around 68 % was obtained for Scots pine impregnated with Imersol-Aqua for 40 min and the highest strength increase of around 10 % was obtained for sessile oak samples impregnated with Imersol-Aqua for 40 min. The highest diagonal tension performance of 879.734 N center dot m was obtained for oak samples impregnated with Imersol-Aqua for 40 min., the lowest diagonal ten-sion performance of 189.111 N center dot m was obtained for Scots pine samples impregnated with Imersol-Aqua for 40 min.
Açıklama
Anahtar Kelimeler
Creative Commons Attribution (CC BY) license, KEYWORDS, paraffin, linseed oil, Imersol-Aqua, diagonal tension, woodworking corner joints
Kaynak
Drvna Industrija
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
73
Sayı
1