Design and optimizations of metal inert gas welding process on different carbon steel alloys

Basit Öğe Kaydı
dc.contributor.advisorÇetin, Muhammet Hüseyin
dc.contributor.authorElgaddafı, Khaled Alı
dc.date.accessioned2024-09-29T18:37:31Z
dc.date.available2024-09-29T18:37:31Z
dc.date.issued2019
dc.departmentLisansüstü Eğitim Enstitüsü, Makine Mühendisliği Ana Bilim Dalıen_US
dc.descriptionFen Bilimleri Enstitüsü, Makine Mühendisliği Ana Bilim Dalıen_US
dc.description.abstractBu çalışmada, östenitik paslanmaz çelik (AISI 304) ve düşük karbonlu çelik (S235JR) malzemenin gaz metal ark kaynak yöntemi kullanılarak farklı akım-voltaj (kaynak enerjisi) değerleri ve tel besleme hızlarında kaynak edilebilirliği araştırılmıştır. Kaynaklı numunelere çekme testi ve sertlik deneyleri yapılarak birleştirilen malzemelerin mekanik özellikleri incelenmiş, sonuçlar Taguchi ve varyans analizi (ANOVA) metodu kullanılarak değerlendirilmiştir. Ayrıca kaynak bölgesinin mikroyapısı incelenerek, ısı tesiri altındaki bölgenin (ITAB) sertlik davranışı açıklanmaya çalışılmıştır. Çekme deneyi sonuçlarına göre deformasyon, kaynak bölgesi dışında, düşük karbonlu çelik bölgesinde meydana gelmiştir. Sertlik değerlerinin analizinde enerji girdisi artışının sertliği azalttığı, tel besleme hızındaki artışın ise sertliği artırdığı belirlenmiştir. Mikroyapı çalışmaları sonucunda, kaynak bölgesinde tane büyümesinin meydana geldiği tespit edilmiştir. ANOVA sonuçlarına göre kaynak bölgesi enerji miktarı ve tel besleme hızı parametreleri kaynak bölgesinin sertlik davranışını %70 oranında açıklayabilmektedir.en_US
dc.description.abstractIn this study, weldability of austenitic stainless steel (AISI 304) and low carbon steel (S235JR) by using gas metal arc welding method under different current-voltage (welding energy) values and wire feed speeds were investigated. The mechanical properties of the joined materials were examined by carrying out tensile tests and hardness tests to the welded specimens and the results were evaluated using Taguchi and analysis of variance (ANOVA) method. In addition, the microstructure of the weld zone was examined and the hardness behavior of the heat affected zone (HAZ) was tried to be explained. According to the tensile test results, deformation was occured in low carbon steel zone outside of welding zone. In the analysis of hardness values, it was determined that increase of energy input decreased hardness and increase of wire feed rate increased hardness. As a result of the microstructure studies, it was observed that the grain growth phenomenon occurred in the welding zone. According to the ANOVA results, the amount of energy in the welding zone and the wire feed rate parameters can explain 70% of the hardness behavior of the welding zone.en_US
dc.identifier.endpage111en_US
dc.identifier.startpage1en_US
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=T1mWGp9MngYYkCSgiJvtVj8mCi0nhI1mXl0miImfhfNk-HzmXimBzEXm04fIIbHW
dc.identifier.urihttps://hdl.handle.net/20.500.14619/14248
dc.identifier.yoktezid545215en_US
dc.language.isoenen_US
dc.publisherKarabük Üniversitesien_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectMakine Mühendisliğien_US
dc.subjectMechanical Engineeringen_US
dc.titleDesign and optimizations of metal inert gas welding process on different carbon steel alloysen_US
dc.title.alternativeFarklı karbon çelik alaşımlarında metal inert gaz kaynak sürecinin tasarımı ve optimizasyonuen_US
dc.typeMaster Thesisen_US