The Effect of Iron Content on Microstructure and Mechanical Properties of A356 Cast Alloy

Küçük Resim Yok

Tarih

2017

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Springer

Erişim Hakkı

info:eu-repo/semantics/closedAccess

Özet

In the present study, microstructure and mechanical properties of A356 alloy including various amounts (0.2 to 1.2 wt pct) of iron were investigated. The alloys were produced by conventional gravity sand casting method. In order to determine the effect of iron addition to A356, optical and scanning electron microscopes (SEM/EDS) were used for microstructural examinations, and X-ray diffraction (XRD) analysis was carried out for phase characterization. Tensile tests were also conducted in order to determine effect of the Fe content on mechanical properties. It was found that as the Fe content of A356 was increased, the secondary dendrite arm spacing (SDAS) was decreased and the morphology of Al-Si eutectic became finer. From XRD examinations, different iron-based intermetallic compounds (beta-Al5FeSi and alpha-Al8Fe2Si) formations were observed. It was also observed that as iron content increased, alpha-Al8Fe2Si intermetallic was transformed into beta-Al5FeSi intermetallic. The tensile test results revealed that tensile strength and elongation values were reduced by increasing Fe content. It was also determined that beta-Al5FeSi intermetallics were more negatively effective on tensile strength than alpha-Al8Fe2Si intermetallics.

Açıklama

Anahtar Kelimeler

Fe-Rich Intermetallics, Si-Mg Alloys, Tensile Properties, Aluminum-Alloys, Oxide-Films, Solidification, Precipitation, Bifilms, Phases, Cu

Kaynak

Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science

WoS Q Değeri

Q2

Scopus Q Değeri

Q1

Cilt

48

Sayı

2

Künye