Synthesis and electrochemical performance of MgFe2O4 with g-C3N4 on Ni-foam as composite anode material in supercapacitors
Küçük Resim Yok
Tarih
2022
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This study aimed to improve the electrochemical performance of MgFe2O4 (MFO) by combining it with g-C3N4 (g-CN). The hydrothermal process was used to produce electrodes directly on the nickel foam surface. XRD, FTIR, SEM, and TEM analyses were made to describe the electrodes in detail. CV, GCD, and EIS measurements were performed electrochemically at various scanning rates and current densities. According to the findings, g-CN-MFO electrode was successfully synthesized in spongy structure on Ni-foams. The areal capacitance (Ca) of g-CN-MFO was measured as 600 mF/cm(2), which is 152% higher than MFO. At the same time, the energy and power densities of g-CN-MFO were calculated to be 13.3 mWh/cm(2) and 200 mW/cm(2) at 1 mA, respectively. EIS results showed that this increase was probably due to easier diffusion of electrolyte ions onto the electrode surface. As a result, the g-CN-MFO electrode can be considered a promising anode material for supercapacitors due to its low cost, ease of fabrication, and strong electrochemical performance.
Açıklama
Anahtar Kelimeler
Electrodes
Kaynak
Journal of Materials Science-Materials in Electronics
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
33
Sayı
30