Comparative Study on Dry and Bio-Corrosive Wear Behavior of Mg-xAl-3Zn Alloys (x=0.5-1-2-3 wt.%)
Küçük Resim Yok
Tarih
2022
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, Mg-xAl-3Zn alloys (x=0.5-1-2-3 wt.%) were produced by the permanent mold casting method. Microstructural characterization of alloys was done with the help of optical microscope (OM) and scanning electron microscope with energy-dispersive spectroscopy (SEM/EDS). Dry and bio-corrosive wear behaviors of alloys were investigated comparatively. Depending on the amount of Al in the alloys, the intermetallic phases were differentiated. Mg17Al12 phase was only observed in Mg-3Al-3Zn alloy distributed along the grain boundary as a continuous or semicontinuous network. The Mg-3Al-3Zn alloy hardness value was about 61.60 +/- 4.23 HV and approximately 30% higher than the other alloys. Dry wear and bio-corrosive (in simulated body fluid (SBF)) wear performances of the alloys were also compared. The abrasive wear mechanism was evident in dry ambient wear due to the intermetallic phases in the structure. Still, the liquid's lubrication effect is much more dominant in the bio-corrosive wear tests carried out in SBF. While Mg-3Al-3Zn wear rate was the lowest in dry wear, it was determined to be the highest in bio-corrosive wear for all applied load conditions. It had been understood that a large amount of Mg17Al12 phase in the structure caused such a result.
Açıklama
Anahtar Kelimeler
AZ series, bio-corrosive wear, dry wear, magnesium
Kaynak
Journal of Materials Engineering and Performance
WoS Q Değeri
Q4
Scopus Q Değeri
Q2
Cilt
31
Sayı
1