Effect of Quenching Rate and Pre-strain on the Strain Ageing Behaviors of 7075 Aluminum Alloys
Küçük Resim Yok
Tarih
2015
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Univ Fed Sao Carlos, Dept Engenharia Materials
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The mechanical properties of aluminum alloys are strongly dependent on the thermo-mechanical process so, the strain ageing behavior of 7075 Al-alloy was investigated in this study. A set of test pieces was solution heat treated at 480 degrees C for 2 h, water quenched (SHTWQ) then pre-strained for 8% in tension. The test samples were aged at 140 degrees C for 0.5, 1, 2, 3, 4, 6, 8, 10, 12, 24, 48, 72 and 96 h in a furnace. The other set of test samples were solution heat treated at 480 degrees C for 2 h, quenched in sand (SHTSQ) then pre-strained for 8% in tension. They were also aged at 140 degrees C for same intervals. The effect of strain ageing, on the mechanical properties of Al-alloy, was investigated by mean of hardness, and tensile tests. The results shown that, the quenching rate after solution heat treatment, ageing time and temperature, as well as pre-strain, play a very important role in the precipitationhardening associated with ageing process of the 7075 Al-alloy.
Açıklama
Anahtar Kelimeler
static strain ageing, Al-alloys, pre-strain, quenching rate, ageing time
Kaynak
Materials Research-Ibero-American Journal of Materials
WoS Q Değeri
Q4
Scopus Q Değeri
Q3
Cilt
18
Sayı
2