A study on the effects of test frequency on the fatigue life of pla parts manufactured by additive manufacturing
Küçük Resim Yok
Tarih
2024
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Fatigue tests of materials require longer time than most other mechanical tests when the enitre process is considered. One of the most critical factors affecting the test time is the test frequency. In this study, fatigue tests at different test frequencies were applied to the PLA parts produced by the additive manufacturing (AM) technique, and the effects of test frequency were investigated. In the fatigue tests, four different stress levels were applied, and the tests were carried out at four different frequencies: 2 Hz, 4 Hz, 6 Hz, and 8 Hz. The fatigue life of the samples changed according to the applied stress levels at varying test frequencies. There was an approximately 44% decrease in the fatigue life found with increasing test frequency at the 1st stress level Fatigue life showed an increasing trend at and after the 3rd stress level. At the 4th stress level, fatigue life increased by 45% when the test frequency was changed from 2 Hz to 8 Hz. In general, after a specific fatigue life, it was observed that increasing test frequency tended to increase the fatigue life.
Açıklama
Anahtar Kelimeler
Kaynak
Gazi Mühendislik Bilimleri Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
10
Sayı
1