The Effect of SiO2 on the Friction Performance of Automotive Brake Friction Materials
Küçük Resim Yok
Tarih
2011
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Natl Acad Sciences Ukraine, Inst Metal Physics
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, 0.5%, 1.0%, 2.0% and 4.0% weighted SiO2 powders were added to bronze-based materials, which are used as friction materials. Blended powders were mixed in three-dimensional mixers to provide a homogeneous mixture. Powders were pressed under pressure of 350 MPa using a single-action press. Pressed samples were sintered at 820 degrees C, for 20 minutes, in ammonia atmosphere. Sintered samples are tested in a wear test device. Wear and friction coefficient tests are carried out on sintered samples. As revealed, with higher amounts of SiO2, the friction coefficient is increased, and the wear ratio is decreased.
Açıklama
Anahtar Kelimeler
friction materials, SiO2, brake lining, wear, friction
Kaynak
Metallofizika I Noveishie Tekhnologii
WoS Q Değeri
Q4
Scopus Q Değeri
Cilt
33
Sayı
3