Wear behaviour of organic asbestos based and bronze based powder metal brake linings
Küçük Resim Yok
Tarih
2005
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Sci Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Bronze based brake linings, were produced by powder metallurgy technique and their wear behaviour was investigated and compared to that of asbestos ones. Bronze powders were compacted under 350, 500 and 600 MPa pressures and sintered at 810 degrees C in ammonia atmosphere for 75 min. For the same friction distance, it was determined that temperature increase in the bronze based brake linings was lower than that of asbestos based ones. However, higher wear rate was observed in the bronze based brake linings. Moreover, thermal conductivity was decreased with high porosity level with low densities. Although, friction coefficient remained the same during breaking, an increase in wear resistance was observed. (C) 2004 Elsevier Ltd. All rights reserved.
Açıklama
Anahtar Kelimeler
powder metallurgy, brake lining, friction materials and wear
Kaynak
Materials & Design
WoS Q Değeri
Q3
Scopus Q Değeri
Cilt
26
Sayı
8