Investigation of the Effect of Ni Amount on the Wear Performance of A356 Cast Aluminum Alloys

Basit Öğe Kaydı
dc.authoridsimsek, dogan/0000-0002-5509-9314
dc.authoridSimsek, Ijlal/0000-0001-6542-8567
dc.authoridsimsek, dogan/0000-0001-8339-9704
dc.contributor.authorSimsek, I.
dc.contributor.authorSimsek, D.
dc.contributor.authorOzyurek, D.
dc.date.accessioned2024-09-29T15:51:23Z
dc.date.available2024-09-29T15:51:23Z
dc.date.issued2020
dc.departmentKarabük Üniversitesien_US
dc.description.abstractThis study investigates the effect of artificial aging treatment on wear performance of A356 alloy containing different amounts of Ni. Within the scope of the study, A356/Ni alloys were produced using the sand mold casting method and then the artificial aging treatment was applied. Alloys were naturally aged at room temperature for 24 hours and artificially aged at 170 degrees C for 10 hours after keeping in solid solution for 8 hours at 540 degrees C and rapidly cooling. The alloys produced were characterized with hardness and density measurements, microstructure examinations, and X-ray diffraction. Wear tests were performed using a pin-on-disc type testing device under three different loads and at four different sliding distances. It was found that alloy density increases with increasing Ni amount. The highest hardness value was obtained for 1% Ni added alloy, and an increase in hardness was observed with the addition of Ni. The lowest weight loss was obtained for 1% Ni added alloy, which also had the highest hardness, and it was observed that the addition of Ni led to an increase in weight loss.en_US
dc.identifier.doi10.1007/s11015-020-00917-w
dc.identifier.endpage1001en_US
dc.identifier.issn0026-0894
dc.identifier.issn1573-8892
dc.identifier.issue9-10en_US
dc.identifier.scopus2-s2.0-85078112094en_US
dc.identifier.scopusqualityQ2en_US
dc.identifier.startpage993en_US
dc.identifier.urihttps://doi.org/10.1007/s11015-020-00917-w
dc.identifier.urihttps://hdl.handle.net/20.500.14619/4025
dc.identifier.volume63en_US
dc.identifier.wosWOS:000519646500013en_US
dc.identifier.wosqualityQ4en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherSpringeren_US
dc.relation.ispartofMetallurgisten_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectA356 alloyen_US
dc.subjectcastingen_US
dc.subjectagingen_US
dc.subjectmicrostructureen_US
dc.subjectwearen_US
dc.titleInvestigation of the Effect of Ni Amount on the Wear Performance of A356 Cast Aluminum Alloysen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu