Pure Bending Fatigue Crack Propagation in Deep-Drawn Steel Cord Filaments
Küçük Resim Yok
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Wires with diameter 0.25 mm from a carbon steel with 0.70 and 0.90% C for tire cords are studied. The effect of the treatment modes, of the carbon content and of the morphology of pearlite on the fatigue resistance of the wires under pure bending tests at a frequency of 10 Hz is determined. The fracture mechanism of the wires is considered. The influence of the microstructure and of the composition of the wires on the trajectory of fatigue cracks is determined with the help of scanning electron microscopy.
Açıklama
Anahtar Kelimeler
steel tire cord, carbon content, pure bending, fatigue crack, fracture surface, cracking mechanism, crack growth