The influence of the heat treatment on mechanical and microstructure properties of Fe-Mn-C high-manganese steel
Küçük Resim Yok
Tarih
2016
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Slovenska Akademia Vied
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The influence of the heat treatment on mechanical properties and microstructures of the Fe-22Mn-0.6C high-manganese steel was investigated at different annealing temperatures. A high-Mn TWIP (Twinning Induced Plasticity) steel specimens (0.6C, 24Mn steel) were fabricated, and were annealed at 700, 900 and 1100 C for 150 min and then air-cooled. The carbide precipitates in the microstructure of specimens were annealed at 700 C. However, the microstructure of specimens annealed at 900 and 1100°C is austenite and some grains include annealing and mechanical twins. The results show that tensile strength of the material decreased, and the ductility of material was improved with increasing annealing temperature. Besides that, hardness value decreased between 700 and 1100 C, which shows a good agreement with the equilibrium dissolution temperature of M3C carbides.
Açıklama
Anahtar Kelimeler
Cold rolling, Heat treatment, High-manganese steel, Microstructure, Sem, TWIP steel
Kaynak
Kovove Materialy
WoS Q Değeri
Scopus Q Değeri
Q3
Cilt
54
Sayı
2