Turning of (Cu-Cr-Zr) alloy with abrasive water jet
Küçük Resim Yok
Tarih
2012
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this research, the effect of the processing parameters on surface roughness during the turning of (Cu-Cr-Zr) alloy with abrasive water jet was studied. In the experimental studies, (Cu-Cr-Zr) alloy, ?30 and 240 mm in size, was processed with abrasive water. In the experiment, pump pressure was 350 MPa, in the form of garnet abrasive and 80 mesh in size and nozzle diameter were kept constant at 1.2 mm. In addition to that in the parameters of nozzle feed rates (10, 15, 20 and 25 mm/min), abrasive flow rates (50, 150, 250 and 350 gr/min) and nozzle distances (2, 5, 8, 11 mm) were used in the tests. According to the results of the experiment, the increase in nozzle feed rate and nozzle distance lead to increase in average surface roughness. On the other hand, the increase in the number of turning speed and abrasive flow rate lead to decrease in average surface roughness. Average surface roughness was measured between 2.5 and 5.5 ?m. © BHR Group 2012 Water Jetting 21.
Açıklama
VLN; Pratt and Whitney; Best High Pressure and Drilling Technology (BHDT); Barton; Gowlings
21st International Conference on Water Jetting: Looking to the Future, Learning from the Past -- 19 September 2012 through 22 September 2012 -- Ottawa, ON -- 95138
21st International Conference on Water Jetting: Looking to the Future, Learning from the Past -- 19 September 2012 through 22 September 2012 -- Ottawa, ON -- 95138
Anahtar Kelimeler
(Cu-Cr-Zr) alloy, Abrasive water jet, Average surface roughness, Lathe
Kaynak
BHR Group - 21st International Conference on Water Jetting: Looking to the Future, Learning from the Past
WoS Q Değeri
Scopus Q Değeri
N/A