Abrasive wear behaviour of cast Al-Si-Mn alloys
Küçük Resim Yok
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Sage Publications Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this paper, the effect of manganese (wt%) and size of the Al2O3 abrasive grains of abrasive wear behaviours of Al-Si-(0.16-0.76%) Mn alloy was examined. Abrasive wear experiments were conducted against abrasive Al2O3 paper grains with diameters in the variety of 38-250 mu m, under the normal load range of 10, 20 and 30 N and the sliding velocity of 0.1 m s(-1). Wear measurements have shown that the wear rate of the material is dependent on the manganese content and the abrasive grain size. The best wear resistance is in the content of 0.73 Mn, which is associated with increased toughness and strength. The Al-Si casting alloy which had 0.73% Mn content exhibited lower wear rate than the Al-Si-0.16/0.22/0.23% Mn alloys after scoured on fine abrasive Al2O3 grains (<65 mu m). Wear experiments achieved on Al2O3 grains having sizes greater than 65 mu m revealed that, the cast Al-Si- alloy which had 0.73% Mn content had lower wear rate than the cast Al-Si-0.16/0.22/0.23% Mn alloys.
Açıklama
Anahtar Kelimeler
Wear, Al-Si alloy, manganese (wt%), abrasion, grain size abrasives
Kaynak
Proceedings of the Institution of Mechanical Engineers Part E-Journal of Process Mechanical Engineering
WoS Q Değeri
Q3
Scopus Q Değeri
Q3
Cilt
233
Sayı
4