Investigation of corrosion properties of box boring din 20MnCr5 steel bars
Küçük Resim Yok
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
EDP Sciences
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
In this study, boriding process was carried out on ? 11 mm diameter DIN 20MnCr5 quality steel bars, used in chain elements such as links and rings, and fasteners such as bolts, at 950oC boronizing temperature, boriding times of 2.5 and 7.5 hours. In this study, the formation and growth of the boride layer and the metallographic structure, the coating thickness and corrosion properties of the boronized steels were investigated depending on the boriding conditions. In the box boriding process, Ekabor-II powder mixture, with its commercial name, was used as boriding powder. According to the optical microstructure results made as a result of box boriding, the coating thickness was 371.5 ?m in the ? 11 mm diameter boronized DIN 20MnCr5 steel bar for 7.5 hours boriding times while it was 195.6 ?m in that steel bar for 2.5 hours boriding times. Corrosion experiments were carried out in solutions prepared by adding 3.5% NaCl to distilled water. According to the results of the immersion test, the lowest corrosion rate in mdd was measured as 112 mg/(dm2 x day) in the ? 11 mm diameter, 7.5 hour boronized sample, and the highest corrosion rate in mdd was 1456.75 mg/(dm2 x day) in the untreated ? 11mm diameter sample. In the potentiodynamic polarization test, parallel results were obtained for immersion corrosion. Corrosion rate values (icor) were measured at the highest value of 209 x 10- 6 A/cm2 in the untreated ? 11 diameter sample, while the lowest icor value was 0.0039 x 10- 6 A/cm2 in the ? 11 mm diameter sample borided for 7.5 hours. © 2023 EDP Sciences. All rights reserved.
Açıklama
5th International Scientific Conference on Construction Mechanics, Hydraulics and Water Resources Engineering, CONMECHYDRO 2023 -- 26 April 2023 through 28 April 2023 -- Tashkent -- 190755
Anahtar Kelimeler
Kaynak
E3S Web of Conferences
WoS Q Değeri
Scopus Q Değeri
N/A
Cilt
401