Tensile test specimen preparing three different cutting method influence on the AA 6061-T6
Küçük Resim Yok
Tarih
2014
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
BHR Group Limited
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Aluminum 6061 (T6) material which is widely used in aviation and defense industries was treated with tensile test in this study. The samples for tensile test were manufactured using three production methods (namely, milling, CO2laser and abrasive water jet (AWJ). Following the tests sample surfaces were assessed for their surface roughness values. Samples which meet the TS EN ISO 6892-1 standard were assessed for their tensile strength, yield strength, percentage elongation and constriction. Among the test samples, sample prepared by milling proved to provide the best surface roughness value (1.32 ?m). The highest tensile strength was obtained from the sample prepared using AWJ while the lowest was obtained from the sample prepared using laser cutting. Samples prepared using abrasive water jet showed 6.57 % difference in terms of tensile strength from samples prepared using milling. © BHR Group 2014 Water Jetting 22.
Açıklama
Air France; Best High Pressure and Drilling Technology (BHDT); et al.; OMAX Corporation; TST; VLN Advanced Technologies Inc
22nd International Conference on Water Jetting 2014: Advances in Current and Emerging Markets -- 3 September 2014 through 5 September 2014 -- Haarlem -- 110163
22nd International Conference on Water Jetting 2014: Advances in Current and Emerging Markets -- 3 September 2014 through 5 September 2014 -- Haarlem -- 110163
Anahtar Kelimeler
Abrasive water jet (AWJ), Aluminum 6061-t6, Laser cutting, Milling, Tensile test